ASTM A – Standard Specification for Annealed or Cold-Worked Austenitic Stainless Steel Sheet, Strip, Plate, and Flat Bar. This standard is a part of ASTM. ASTM A March 10, Standard Specification for Annealed or Cold- Worked Austenitic Stainless Steel Sheet, Strip, Plate, and Flat Bar. This specification. ASTM A – Designation: A – 10 Standard Speci?cation for Annealed or Cold-Worked Austenitic.

Author: Kagajora Kagaran
Country: Eritrea
Language: English (Spanish)
Genre: Literature
Published (Last): 24 July 2017
Pages: 25
PDF File Size: 8.17 Mb
ePub File Size: 1.23 Mb
ISBN: 171-6-16873-845-4
Downloads: 5199
Price: Free* [*Free Regsitration Required]
Uploader: Mikadal

This standard has been approved for use by agencies of the Department of Defense. If you feel that your comments have not received a fair hearing you should make your views known to the ASTM Committee on Standards, at the address shown below.

Only annealed conditions of grades speci?

Chemical equipment and piping, heat exchanger components, dairy and food handling equipment and utensils, cryogenic vessels and components, architectural and structural applications exposed to non-marine atmospheres. Rockwell B 95 95 Type L LN Types and L are weldable by most fusion or resistance welding techniques. Type L Stainless Steel is preferred in welding applications to exclude the formation of chromium carbides during cooling in the heat affected region of the weld.

Due to the high work hardening rate of these materials, intermediate anneals maybe required to successfully fabricate the part.

Number of Tests 8. The choice of test method for materials in conditions other than annealed shall be at the option of the seller.

C Annealed material that naturally meets mechanical properties may be applied. Annealed Types and L can be fabricated by roll forming, deep drawing, bending and most other fabrication techniques.

Related Posts (10)  FORD AXOD PDF

Depending on the work hardening characteristics of the particular grade, either the yield or the tensile strength can be the controlling factor in meeting the properties.

ASTM A for Annealed or Cold-Worked Austenitic Stainless Steel Sheet, Strip, Plate, and Flat Bar

Heat to o F to zstm F and cool at sufficiently high rates through oF to oF to avoid precipitation of chromium carbides. Maximum unless otherwise indicated. A — 10 Standard Speci? Originally approved in D PSS means plate, strip, sheet.

and L Stainless Steel – NKS

X666-10 rights to photocopy the standard may also be secured from the ASTM website www. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk of infringement of such rights, are entirely their own responsibility.

Hard Elongation in 2 in. In the annealed condition it is essentially non-magnetic and becomes slightly magnetic with the application of cold work.

Type L should be used in heavier sections to reduce the occurrence of carbide precipitation in the heat affected region adjacent to the weld pool. However, in the case of dispute, tests shall be made by pressure.

Find out what NKS can do for you. If filler metal is required, Type is normally used. HardC Elongation in 2 in. This revision of Speci? Chemical equipment and piping, heat exchanger components, dairy and food handling equipment and utensils, cryogenic vessels and components, architectural and structural applications exposed to non-marine atmospheres Chemical Composition: Type L should be used in heavier sections to reduce the occurrence of carbide precipitation in the heat affected region adjacent to the weld pool Corrosion: Your comments will receive careful consideration at a meeting of the responsible technical committee, which you may attend.

Related Posts (10)  BELIMO LF 120 PDF

Last previous edition approved in as A — Individual reprints single or multiple copies of this standard may be obtained by contacting ASTM at the above address or at phonefaxor service astm. The values obtained in this manner should not, however, be taken as the actual yield strength for 0.

304 and 304L Stainless Steel

In case of dispute, the offset method of determining yield strength shall be used. Types and L provides corrosion resistance in a wide range of moderately oxidizing and reducing conditions, fresh water and non-marine applications.

The noncontrolling factor normally will exceed considerably the speci? The values given in parentheses are for information only. These alloys represent an excellent combination of corrosion resistance and a666-1. Types and L cannot be hardened by thermal a66-610.

B Type is generally produced with a chemical composition balanced for rich side Type or lean side Type austenite stability depending on the properties required for speci? Your comments are invited either for revision of this standard or for additional standards x666-10 should be addressed to ASTM International Headquarters.

Current edition approved Sept. A number in parentheses indicates the year of last reapproval. Specimens shall be bent around a diameter equal to the product of the 6a66-10 factor times the speci?

This standard is subject to revision at any time by the responsible technical committee and must be reviewed every? Material Test Report and Certi?

HRC typical L Ann 25 min. One bend test shall be made from one end of each coil.